Aeineh N, Sharifi N, Behjat A. Application of Au@SiO2 Plasmonic Nanoparticles at Interface of TiO2 Mesoporous Layers in Perovskite Solar Cells. IJOP. 2018; 12 (2) :99-108
URL: http://ijop.ir/article-1-297-fa.html
Application of Au@SiO2 Plasmonic Nanoparticles at Interface of TiO2 Mesoporous Layers in Perovskite Solar Cells. نشریه انجمن اپتیک و فوتونیک ایران. 1397; 12 (2) :99-108

URL: http://ijop.ir/article-1-297-fa.html


چکیده:   (1280 مشاهده)

To investigate the plasmonic effect in perovskite solar cells, the effect of depositing Au@SiO2 nanoparticles on the top and the bottom of mesoporous TiO2 layers was studied. First, Au@SiO2 nanoparticles were synthesized. The particles were then deposited at the different interfaces of mesoporous TiO2 layers. Although the two structures show approximately similar optical absorption, only cells with Au@SiO2 nanoparticles deposited at the bottom of the mesoporous TiO2 layers demonstrated an improved photocurrent performance compared to the reference cells. This structure shows a short-circuit current density (JSC) of 20.7 mA/cm2 and open circuit voltage of 1081 mV. This enhancement may be attributed either to the interface surface engineering or plasmonic resonance of Au@SiO2 nanoparticles depends to the NPs size and position.  

متن کامل [PDF 635 kb]   (310 دریافت)    
نوع مطالعه: پژوهشي | موضوع مقاله: تخصصي
دریافت: ۱۳۹۵/۹/۲۸ | ویرایش نهایی: ۱۳۹۷/۱۰/۱۵ | پذیرش: ۱۳۹۶/۴/۱۱ | انتشار: ۱۳۹۷/۹/۲۱

ارسال نظر درباره این مقاله : نام کاربری یا پست الکترونیک شما:
CAPTCHA

کلیه حقوق این وب سایت متعلق به نشریه انجمن اپتیک و فوتونیک ایران می باشد.

طراحی و برنامه نویسی : یکتاوب افزار شرق

© 2019 All Rights Reserved | International Journal of Optics and Photonics

Designed & Developed by : Yektaweb