en عمومى General پژوهشي Research <div style="text-align: justify;">In this study, a sol-gel peroxotungstic acid sol was employed to deposit tungsten oxide (WO₃) films by the spin-coating technique. In view of smart window applications, electrochromic windows were then designed and fabricated using a thin tungsten oxide film. For this purpose, Glass/ FTO/ WO₃/ electrolyte/ FTO/Glass could be of use due to its special structure that consists of an electrochromic layer (WO₃) on a transparent conductor (FTO), an electrolyte containing Li⁺ cations, and a transparent conductor layer. A voltage was applied on the fabricated sample, which was later assesed for its transmission, switching speed, and coloration efficiency. An increase in the coloration efficiency from 87 cm²/C^-1 to 99.1 cm²/C^-1 was found associated with an increase in the deposition speed. Moreover, the increase in the deposition speed led to a decrease in the coloration and bleaching time duration from 11.4 s to 6.2 s and from 12.8 s to 5.2 s respectively. The results obtained on the thin film WO₃ can be useful for electrochromic applications.</div> Electrochromic material, Sol-gel preparation, Tungsten oxide, Coloration. 79 88 http://ijop.ir/browse.php?a_code=A-10-518-2&slc_lang=en&sid=1 Nayyereh Daroogheh Nd1990@chamil.ir 10031947532846002663 10031947532846002663 No Department of Physics, Faculty of Physics, University of Kashan Elham Karimi Karimi_6800@yahoo.com 10031947532846002664 10031947532846002664 No Department of Physics, Faculty of Physics, University of Kashan S.M. Bagher Ghorashi mghorashi@kashanu.ac.ir 10031947532846002665 10031947532846002665 Yes Department of Physics, Faculty of Physics, University of Kashan